CXT8113 natural is a high purity, high transparency, amorphous, thermoplastic polyamide, based on cycloaliphatic monomers. Compared with semi-crystalline nylon, CXT8113 avoid crystallizing by selecting specific monomers and becomes an other amorphous polymer which has high transparency. Meanwhile, CXT8113 combine the properties of semi-crystalline nylon and amorphous nylon which makes it be the first choice in the present market.

Composition PAMACM12

Permanent transparency and high light transmission

High dimensional stability and easy processing

Excellent abrasion and scratch resistance

Superior impact resistance to high / low temperature

Good chemical and solvent resistance

High level of UV resistance and weathering stability

High stress crack resistance

High flexural fatigue strength and high memorability

Low density and light quality

Easily colorable and food contact approval

Features

Optics		Packaging
Frames, Lens, Optical components etc.		Cosmetics packaging, Medical packaging, etc.
Food Contact		Industry
Feeder, Coffee machine, Cup, etc.		Auto parts(oil cup, etc), Mechanical engineering.
Ectronic Products		Consumer Goods
Headphone, Ear-Hook, etc.		Sports & Leisure, Tools & Accessories, etc.

Items	Unit	Test Method	Values
Charpy notched impact	KJ/m²	GB/T 1043-93	17
Charpy non-notched impact	KJ/m²	GB/T 1043-93	25JNB
Tensile strength	MPa	GB/T 1040-92	65
Elongation at break	%	GB/T 1040-92	160
Flexural strength	MPa	GB 9341-2000	70
Flexural modulus	MPa	GB 9341-2000	1780
Density	g/cm³	GB 1033-86	1.01
Heat distortion temperature(0.45 MPa)	ºC	GB1634-79	135
Light transmittance	%	--	92
Shore D hardness	--	GB 2411-80	83